Closely pitched polysilicon fuses and method of forming the same

ABSTRACT

A method for decreasing the pitch of polysilicon fuses uses tungsten barriers formed adjacent to the fuse elements. The tungsten barriers are made compatible with the process to form a crack stop by stacking tugsten at the via level on top of the tungsten at the contact level in the crack stop. An interlevel dielectric is used as a cover for the fuse.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. application Ser. No. 08/903,439, filed on Jul. 30, 1997, now U.S. Pat. No. 5,955,773, which is a continuation of U.S. application Ser. No. 08/699,830, filed on Aug. 20, 1996, now abandoned.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention generally relates to the manufacture of polysilicon fuses in semiconductor devices and, more particularly, to a method of forming closely pitched polysilicon fuses which allows the density of fuses to be increased without the risk of damaging adjacent fuses when a fuse is blown.

2. Background Description

Crack stops are employed in silicon chip processing to reduce damage caused by chip dicing. A crack stop is typically a narrow trench etched down to the silicon substrate around the chip. A common method of forming the crack stop is to form a tungsten-filled trench around the chip, expose the tungsten (W) trench, and wet etch out the tungsten using hydrogen peroxide.

Fuse arrays are commonly formed in very large scale integrated (VLSI) circuits. The purpose of the fuses may be variously to customize the semiconductor device for a specific application or to disconnect a defective part of the device leaving a redundant part connected. The preferred manner of blowing a fuse is by laser ablation, but this creates a pit which limits how closely spaced fuses can be in the array to avoid damaging adjacent fuses.

It is known to use tungsten fuse barriers in aluminum/copper (AlCu) alloy fuses in order to protect adjacent fuses; however, tungsten fuse barriers are not compatible with the standard polysilicon fuse/crack stop process. This is because, in standard processing, the terminal via reactive ion etching (RIE) which thins the insulator above the polysilicon fuse also exposes the tungsten crack stop. If a tungsten fuse barrier were present, it would be removed when the tungsten crack stop was removed with the hydrogen peroxide etch.

SUMMARY OF THE INVENTION

It is therefore an object of the present invention to provide a method of forming closely pitched polysilicon fuses using tungsten fuse barriers in order to permit closely pitched polysilicon fuses.

According to the invention, there is provided a method for decreasing the pitch of polysilicon fuses in which tungsten barriers are formed adjacent to the fuse elements and then making the tungsten barriers compatible with a process to form a crack stop. In the preferred embodiment, the tungsten is stacked at the via level on top of the tungsten at the contact level in the crack stop and an interlevel dielectric is used as a cover for the fuse. In this way, the tungsten fuse barrier process is made compatible with the polysilicon fuse/crack stop process.

BRIEF DESCRIPTION OF THE DRAWINGS

The foregoing and other objects, aspects and advantages will be better understood from the following detailed description of a preferred embodiment of the invention with reference to the drawings, in which:

FIG. 1 is a cross-sectional view of a known tungsten barrier crack stop and polysilicon fuse structure;

FIG. 2 is a cross-sectional view showing the structure of FIG. 1 after a hydrogen peroxide etch to remove the tungsten in the crack stop trench;

FIG. 3 is a cross-sectional view of stacked tungsten barrier crack stop and a polysilicon fuse using tungsten barriers according to the invention;

FIG. 4 is a cross-sectional view showing the structure of FIG. 3 after a hydrogen peroxide etch to remove the tungsten in the crack stop trench;

FIG. 5 is a plan view showing the relative spacing of polysilicon fuses using conventional techniques without tungsten barriers; and

FIG. 6 is a plan view showing the relative spacing of the polysilicon fuses with tungsten barriers according to the invention.

DETAILED DESCRIPTION OF A PREFERRED EMBODIMENT OF THE INVENTION

Referring now to the drawings, and more particularly to FIG. 1, the process for forming a conventional crack stop and polysilicon fuse will first be described to illustrate the novel features of the invention. In FIG. 1, there is shown in cross-section a conventional crack stop formed in semiconductor device. This crack stop is formed around the periphery of the device. FIG. 1 also shows in cross-section a conventional polysilicon fuse formed elsewhere in the semiconductor device. The fuse may be constituted as the gate structure of a metal oxide semiconductor (MOS) device formed in an array of such devices.

The crack stop and the fuse shown in FIG. 1 are formed as part of the process of manufacturing the semiconductor device. Beginning with a substrate 10, the polysilicon fuse 11 is first patterned on the substrate. Then a layer 12 of phosphorous silicate glass (PSG) is deposited. PSG is a phosphorous doped silicon dioxide (SiO₂). The PSG layer 12 is then etched in a ring shape near the periphery of the semiconductor device, and a tungsten (W) fill 13 is deposited at the contact level (CT) to form the crack stop in the etched ring shaped area. At the same time, tungsten contacts 17 are formed in etched areas of the PSG 12. A first metalization layer (M1), constituting a first wiring layer in electrical contact with the tungsten contacts 17, is typically formed on the PSG layer 12. Next, an interlayer dielectric (ILD) layer 14 is deposited. A damascene wiring level may be formed in the ILD layer 14 or a second metalization layer (M2) constituting a second wiring level may be formed on top of the ILD layer 14. The choice depends on the specific semiconductor device and process used. In the example illustrated, the ILD layer 14 is etched in selected areas to the first metalization layer (M1) and tungsten deposited to form tungsten vias 18. A second metalization layer (M2) in electrical contact with the vias 18 is then formed on the ILD layer 14. A final passivation layer 15 is next deposited. This layer may be, for example, silicon dioxide (SiO₂) or silicon nitride (Si₃ N₄). A polyimide layer 16 is then deposited over the final passivation layer 15. The device is then patterned and etched to expose the tungsten fill 13 at the contact level. A thin oxide remains over the polysilicon fuse 11 as shown in FIG. 1. This thin oxide serves as an encapsulation of the fuse which is part of the device wiring unless blown. In the final processing step, the device is dip etched in hydrogen peroxide (H₂ O₂) to etch the tungsten in the crack stop trench, resulting in the structure shown in FIG. 2. If a tungsten barrier between the polysilicon fuses 11 were included, it would be exposed with the tungsten 13 of the crack stop and removed along with the crack stop tungsten during the hydrogen peroxide etch.

FIG. 3 shows in cross-section the crack stop and the polysilicon fuse with tungsten barriers according to the invention. Beginning with a substrate 20, the polysilicon fuse 21 is first patterned on the substrate, and then a layer 22 of phosphorous silicate glass (PSG) is deposited as before. The PSG is then etched in barrier areas on either side of the polysilicon fuses 21 and in a first ring shaped area near the periphery of the semiconductor device. A first tungsten (W) fill is then deposited at the contact level (CT) to form the tungsten barrier areas 29 and the crack stop 23. A first metalization layer (M1) is formed on the PSG layer 22. Next, an interlayer dielectric (ILD) layer 24 is deposited. The ILD layer is then etched to expose the first tungsten fill 23 of the crack stop, forming a second ring at the via level. This second ring is then filled with a second tungsten fill 30 deposited on top of the first tungsten fill 23. Note that in the crack stop, the tungsten fill 23 at the contact level and the tungsten fill 30 at the via level are stacked. Again, a damascene wiring level may be formed in the ILD layer 24 or, as shown in FIG. 3, a second metalization layer (M2) constituting this wiring level may be formed on top of the ILD layer 24. A final passivation layer 25 is next deposited. As before, this layer may be, for example, silicon dioxide (SiO₂) or silicon nitride (Si₃ N₄). A polyimide layer 26 is then deposited over the final passivation layer 25. The device is then patterned and etched to expose the tungsten fill 30 at the via level. A thin oxide and a thin ILD remains over the polysilicon fuse 21 as shown in FIG. 3. In the final processing step, the device is dip etched in hydrogen peroxide (H₂ O₂) to etch the stacked tungsten via and contact levels of the crack stop, as shown in FIG. 4. A brief etch would also be required, followed by another hydrogen peroxide etch, if a tungsten-via liner was employed. Tungsten-via liners are used to reduce tungsten-via resistance.

FIGS. 5 and 6 show the relative improvement in fuse pitch afforded by the invention. FIG. 5 shows a partial array of polysilicon fuses with a spacing of 4.5 μm, which is currently a closely spaced as the fuses can be made without a high risk of damaging adjacent fuses with a fuse is blown by laser ablation. FIG. 6 shows a partial array of polysilicon fuses with alternating tungsten barriers. With the addition of the tungsten barriers, the spacing has been reduced to 1.8 μm in a specific implementation.

Thus, the invention allows the use of tungsten fuse barriers in a process that is compatible with polysilicon fuse manufacture. This, in turn, permits forming closely pitched polysilicon fuses so that higher density fuse arrays can be achieved without the possibility of damaging adjacent fuses when a fuse is blown.

While the invention has been described in terms of a single preferred embodiment, those skilled in the art will recognize that the invention can be practiced with modification within the spirit and scope of the appended claims. 

Having thus described my invention, what I claim as new and desire to secure by Letters Patent is as follows:
 1. A semiconductor substrate comprising a plurality of individual semiconductor chips, said semiconductor substrate comprising:tungsten fuse barriers adjacent to a polysilicon fuse wherein said polysilicon fuse is covered by first and second dielectric materials and the tungsten fuse barriers are covered by said second dielectric material; and a crack stop positioned between said individual semiconductor chips for protecting said individual semiconductor chips when said chips are diced from said semiconductor substrate, wherein said crack stop comprises a wide channel in an upper portion of said second dielectric material and a narrower channel in a lower portion of said second dielectric material and said first dielectric material. 